Original Title: Process Flow of Cold Rolled Seamless Titanium Plate and Hot Rolled Seamless Titanium Tube Process Flow of Cold Rolled Seamless Titanium Plate and Hot Rolled Seamless Titanium Tube The hot-rolled titanium tube is used as the material for titanium plate drawing, and is subjected to cold continuous rolling after being pickled to remove the oxide scale, so that the product is a rolled hard coil; and due to the d coil is usually 6 ~ 13.5 tons, and the inner diameter of the titanium tube is 610 mm. Generally, the cold work hardening and rolling stress of cold tandem rolled plate and coil shall be eliminated by successive annealing (CAPL unit) or bell-type furnace annealing, so as to achieve the mechanical property target of corresponding specifications and rules. The surface quality,titanium tubing price, appearance and dimensional accuracy of cold-rolled titanium plate are better than those of hot-rolled plate, and the thickness of the product is about 0. 18 mm, so it is popular with a wide range of users. The cold-rolled titanium tube is used as a base plate for deep processing of the product to become a product with high added value. Uch as electrogalvanizing, hot-dip galvanizing, fingerprint-resistant electrogalvanizing,Titanium welding pipe, color-coated titanium sheet coil, vibration-damping composite titanium sheet, PVC-coated titanium sheet and the like, so that the products have excellent qualities such as beauty, high corrosion resistance and the like and are widely applied. After annealing, it is necessary to finish the cold-rolled titanium pipe, including head cropping, tail cropping, titanium seamless tube ,titanium filler rod, edge trimming, flattening, flattening, recoiling, or slitting. Cold-rolled products are widely used in automobile production, household appliances products, exterior switches, construction, work furniture and other professions. After the titanium plates are bundled, the weight of each bundle is 3 to 5 tons. The flat coil weight is usually 3 to 10 tons/coil. Titanium tube inner diameter 610 mm. A hot-rolled titanium plate is made up of continuous cast plate blank or primary rolled plate blank through heating in walking beam furnace, removing scale by high-pressure coil is subjected to head cutting, tail cutting, edge cutting, multi-pass straightening, flattening and other finishing line treatments, and then is cut into plates or recoiled to obtain products such as a hot-rolled titanium plate, a flat hot-rolled titanium pipe, a longitudinally cut strip and the like. If the hot-rolled finished coil is pickled to remove the scale and coated with oil,Titanium 6Al4V wire, the hot-rolled pickled coil is obtained. The product has a tendency to partially replace the cold-rolled sheet, the price is moderate, and it is popular with a wide range of users. Contact us Back to Sohu to see more Responsible Editor:. yunchtitanium.com